ColorWhitePhysical formPowder
-
CAS No.13462-67-7Purity96%~98.5%
-
Model NumberXM-A100Appearancewhite Powder
-
Applicationplastic coating paint printing inkClassificationTitanium Dioxide
-
Grade StandardIndustrial GradeMolecular FormulaTiO2
-
Other Namestio2CertificationISO9001
-
HS code3206111000Package25kg/bag
-
PH Value6.5-8.5TiO2 Content96~98.5%
-
Oil Absorption21~26Residue on sieve 45 μm %0.03~0.05
-
Matter volatile at 105°C %0.3~0.5Tinting strength %95~109
-
SampleFreely Provided
A paint-development brief should identify the pigment candidate before discussing the finished appearance. XM-A100 is an industrial titanium dioxide white powder with a stated TiO2 content of 96–98.5%, offered for paint and related coating, plastic and printing-ink formulation enquiries.
Make XM-A100 part of a defined paint comparison
Describe the paint system and the pigment requirements that will determine whether XM-A100 proceeds to a trial. Request the crystal form and any surface treatment specified for the offered material. The model code is an identifier, not evidence of a particular phase or a guaranteed finished-film result.
Keep residue and volatile tests in their measurement context
XM-A100 has a stated residue of 0.03–0.05% on a 45 μm sieve and volatile matter of 0.3–0.5% at 105°C. Match the measurement methods when comparing those values with another pigment. Consider the pH range of 6.5–8.5 within the grade assessment rather than relying on TiO2 content alone.
Ask for a usable tinting comparison
Before interpreting the XM-A100 tinting-strength figure, establish its reference and test procedure. The oil-absorption figure also needs defined units and conditions. Those details help a paint developer design a meaningful comparison without treating incomplete numbers as proof of optical performance.
For an XM-A100 enquiry, specify the intended paint or ink and the acceptance test that will decide pigment selection. A matched technical specification and controlled formulation comparison give this industrial TiO2 candidate a practical role in development.